VERIFICATION #11a Thin film calculation result. Recall that you can choose from multiple substrate materials such as silicon, GaAs, or InP and from deposition materials such as gold or silver.


Input string: 59.348,2.3,0 101.11,1.35,0 59.348,2.3,0 101.11,1.35,0 59.348,2.3,0
Total number of films entered: 5      Incident angle: 30 degrees    Index of ambient material(n,k)=1      Fixed index of substrate (ns,ks)=1.52      Units for thickness and wavelength should be nm.
Nomenclature is as follows: perp refers to s-polarization ; para refers to p polarization ; mag means magnitude.
The following are the field and power, as well as the phase shift for both polarization states. Both reflected and transmitted values are given.
References:
[1] Born and Wolf, Principles of Optics, 7th ed. Chapter 1
[2] Steve Byrnes, http://sbyrnes321.byethost11.com/
ACKNOWLEDGEMENT: Luxpop would like to thank (i) Steve Byrnes of Berkeley for his valuable assistance in correcting previous errors, and (ii) Didier Dutartre for his contribution.

lambda (nm) mag r_perp (field) R_perp (power) mag r_para (field) R_para (power) delta r_phase perp delta r_phase para mag t_perp (field) T_perp (power) mag t_para (field) T_para (power) delta t_phase perp delta t_phase para
396 0.4554 0.20741 0.2827 0.07991 -1.861 1.551 0.6915 0.79259 0.7451 0.92009 -2.880 -2.629
426 0.8361 0.69907 0.7099 0.50390 -2.408 0.982 0.4261 0.30093 0.5471 0.49610 2.553 2.770
456 0.9228 0.85155 0.8518 0.72551 -2.733 0.556 0.2993 0.14845 0.4069 0.27449 2.120 2.248
486 0.9467 0.89625 0.8956 0.80203 -2.941 0.271 0.2502 0.10375 0.3456 0.19797 1.841 1.902
516 0.9529 0.90797 0.9072 0.82299 -3.102 0.051 0.2356 0.09203 0.3268 0.17701 1.624 1.633
546 0.9507 0.90385 0.9030 0.81550 3.041 -0.141 0.2408 0.09615 0.3336 0.18450 1.435 1.399
576 0.9418 0.88704 0.8863 0.78556 2.908 -0.323 0.2611 0.11296 0.3597 0.21444 1.255 1.176
606 0.9248 0.85524 0.8551 0.73111 2.773 -0.507 0.2955 0.14476 0.4028 0.26889 1.075 0.952
636 0.8956 0.80219 0.8040 0.64649 2.630 -0.699 0.3455 0.19781 0.4618 0.35351 0.883 0.716
666 0.8473 0.71797 0.7259 0.52691 2.472 -0.906 0.4125 0.28203 0.5343 0.47309 0.670 0.461
696 0.7691 0.59159 0.6139 0.37692 2.295 -1.122 0.4964 0.40841 0.6131 0.62308 0.428 0.182

History: updated Mar/31/2012 after code update Questions? Comments? Contact us   ||    Use of this website indicates acceptance of the terms and conditions.