VERIFICATION #12a Thin film calculation result. Recall that you can choose from multiple substrate materials such as silicon, GaAs, or InP and from deposition materials such as gold or silver.


Input string: 59.348,2.3,0 101.11,1.35,0 59.348,2.3,0 101.11,1.35,0 59.348,2.3,0
Total number of films entered: 5      Incident angle: 30 degrees    Index of ambient material(n,k)=1      Material of substrate: SF10       Units for thickness and wavelength should be nm.
Nomenclature is as follows: perp refers to s-polarization ; para refers to p polarization ; mag means magnitude.
The following are the field and power, as well as the phase shift for both polarization states. Both reflected and transmitted values are given.
References:
[1] Born and Wolf, Principles of Optics, 7th ed. Chapter 1
[2] Steve Byrnes, http://sbyrnes321.byethost11.com/
ACKNOWLEDGEMENT: Luxpop would like to thank (i) Steve Byrnes of Berkeley for his valuable assistance in correcting previous errors, and (ii) Didier Dutartre for his contribution.

lambda (nm) mag r_perp (field) R_perp (power) mag r_para (field) R_para (power) delta r_phase perp delta r_phase para mag t_perp (field) T_perp (power) mag t_para (field) T_para (power) delta t_phase perp delta t_phase para
396 0.5073 0.25734 0.3399 0.11553 -1.950 1.457 0.6135 0.74266 0.6695 0.88447 -2.853 -2.620
426 0.8296 0.68825 0.7071 0.49998 -2.438 0.935 0.3993 0.31175 0.5057 0.50002 2.619 2.818
456 0.9136 0.83474 0.8396 0.70498 -2.742 0.539 0.2917 0.16526 0.3897 0.29502 2.169 2.288
486 0.9388 0.88126 0.8837 0.78094 -2.945 0.266 0.2479 0.11874 0.3367 0.21906 1.867 1.924
516 0.9455 0.89401 0.8959 0.80268 -3.103 0.050 0.2347 0.10599 0.3202 0.19732 1.629 1.638
546 0.9433 0.88988 0.8918 0.79538 3.042 -0.138 0.2396 0.11012 0.3267 0.20462 1.422 1.387
576 0.9340 0.87238 0.8749 0.76543 2.912 -0.316 0.2583 0.12762 0.3503 0.23457 1.228 1.152
606 0.9164 0.83974 0.8437 0.71181 2.780 -0.494 0.2898 0.16026 0.3887 0.28819 1.035 0.919
636 0.8870 0.78681 0.7941 0.63066 2.643 -0.677 0.3346 0.21319 0.4405 0.36934 0.834 0.677
666 0.8401 0.70578 0.7207 0.51937 2.494 -0.870 0.3935 0.29422 0.5029 0.48063 0.617 0.421
696 0.7675 0.58900 0.6188 0.38297 2.331 -1.068 0.4654 0.41100 0.5702 0.61703 0.376 0.149

History: (1) updated Mar/31/2012 after code update (2) code was updated Apr/2015 to call up N-SF10 instead of SF10. Negligible change not impacting greater than 5th or 4th sig fig on all mag and phase values Questions? Comments? Contact us   ||    Use of this website indicates acceptance of the terms and conditions.