VERIFICATION #16b Thin film result Thin film calculation result. Recall that you can choose from multiple substrate materials such as silicon, GaAs, or InP and from deposition materials such as gold or silver.

Input string: 5.348,{Al} 101.11,1.35,0 5.348,{Si} 101.11,1.35,0 59.348,2.3,0
Total number of films entered: 5      Incident angle: 30 degrees     Index of ambient material(n,k)=1      Material of substrate: InP       Units for thickness and wavelength should be nm.
Nomenclature is as follows: perp refers to s-polarization ; para refers to p polarization ; mag means magnitude.
The following are the field and power, as well as the phase shift for both polarization states. Both reflected and transmitted values are given.
References:
[1] Born and Wolf, Principles of Optics, 7th ed. Chapter 1
[2] Steve Byrnes, http://sbyrnes321.byethost11.com/
ACKNOWLEDGEMENT: Luxpop would like to thank (i) Steve Byrnes of Berkeley for his valuable assistance in correcting previous errors, and (ii) Didier Dutartre for his contribution.

lambda (nm) Set of thicknesses Input power mag r_perp (field) R_perp (power) mag r_para (field) R_para (power) delta r_phase perp delta r_phase para mag t_perp (field) T_perp (power) mag t_para (field) T_para (power) delta t_phase perp delta t_phase para
730.0 1 1.0 0.7965 0.6344 0.7415 0.5498 -2.883 0.335 0.2248 0.2007 0.2535 0.2552 3.090 3.103
754.0 1 1.0 0.7798 0.6081 0.7230 0.5228 -2.902 0.310 0.2301 0.2101 0.2581 0.2642 2.975 2.994
778.0 1 1.0 0.7606 0.5784 0.7017 0.4924 -2.916 0.291 0.2364 0.2213 0.2640 0.2762 2.860 2.887
802.0 1 1.0 0.7369 0.5430 0.6755 0.4564 -2.925 0.278 0.2441 0.2356 0.2719 0.2924 2.752 2.786
826.0 1 1.0 0.7121 0.5071 0.6481 0.4201 -2.922 0.281 0.2539 0.2546 0.2822 0.3146 2.631 2.674
850.0 1 1.0 0.6855 0.4699 0.6184 0.3824 -2.908 0.294 0.2637 0.2747 0.2928 0.3385 2.514 2.565
874.0 1 1.0 0.6600 0.4356 0.5896 0.3476 -2.880 0.325 0.2735 0.2954 0.3035 0.3637 2.390 2.451
898.0 1 1.0 0.6454 0.4165 0.5715 0.3266 -2.830 0.382 0.2813 0.3124 0.3126 0.3858 2.247 2.320
922.0 1 1.0 0.6437 0.4143 0.5664 0.3208 -2.774 0.448 0.2851 0.3206 0.3180 0.3991 2.101 2.185
946.0 1 1.0 0.6648 0.4419 0.5851 0.3424 -2.719 0.517 0.2820 0.3135 0.3175 0.3973 1.937 2.034
970.0 1 1.0 0.6917 0.4784 0.6122 0.3748 -2.702 0.543 0.2696 0.2839 0.3070 0.3684 1.809 1.910

History:
Updated to rev (a) Apr/28/2012 after code update for T para.
Updated to rev (b) Dec/2/2012 after selection of Palik ref for Si. ==>Minor change in fourth decimal place for most results.Questions? Comments? Contact us   ||    Use of this website indicates acceptance of the terms and conditions.